Materials development and CO2 adsorption methods

https://doi.org/10.1039/C8TA06224B “Porous siliceous cellular foams (SCFs) with variable pore and window sizes were synthesised using a modified version of the micro-emulsion method reported earlier by

https://doi.org/10.3390/pr8121531 “The experimental campaign concerning tests of CO2 adsorption was carried out in a laboratory-scale fluidization column made of plexiglas, with an internal diameter of 50

https://doi.org/10.1093/ce/zkac020 “The adsorption of CO2 was carried out at 25°C and atmospheric pressure using 15/85 vol% CO2/N2 as a feed gas representing the concentration of CO2 in the

https://doi.org/10.1093/ce/zkac020 “Hexagonal mesoporous silica MCM-41 was synthesized by dissolving 2 g of pore-generating agent, CTAB, with 120 mL of deionized water under constant agitation. After

https://doi.org/10.3390/inorganics10070087 “Ordered hierarchical porous silica materials with micro/mesoporous structures were prepared using dextran as a template via the sol-gel technique. First, an aqueous–alcoholic dextran solution

https://doi.org/10.1039/D0RA04497K “WG, W and HAc were mixed with a volumetrical ratio of 6 : 33 : 1.2 under room temperature (25 °C) to form a water glass solution. The

https://doi.org/10.1590/1980-5373-MR-2019-0285 “Monolith M1 was prepared using tetraethoxysilane (TEOS) as a silica source and the cetyltrimethylammonium bromide (CTAB) as surfactant. The methodology for the preparation of

https://doi.org/10.1016/j.ces.2014.05.018 “Fig. 1 shows the schematic and a photograph of the BFB reactor system designed and built for the evaluation of CO2 capture and regeneration using solid

https://doi.org/10.1093/ce/zkac020 “The CO2 adsorption efficiency of the adsorbent was presented as an adsorption capacity (Qads) that was determined by plotting between Cou/Cin versus time to obtain a breakthrough

https://doi.org/10.1093/ce/zkac020 “The adsorption of CO2 was carried out at 25°C and atmospheric pressure using 15/85 vol% CO2/N2 as a feed gas representing the concentration of CO2 in the